arrow "a", Fig. 1. Arrow "b" indicates a pit in the camber surface. Arrows "c" indicate some of the shallow grooves resulting from scratches on the fracture surface.
HEN IT involves an airplane, even the seemingly insignificant things can be most important. The tiny little dots and nicks can be the start of corrosive actions which can result in dire consequences. One such case was recently passed on to SPORT AVIATION by the Bureau of Aviation Safety of the National Transportation Safety Board, with a recommendation that it be published in order to bring such a situation to the attention of the flying public in the interest of accident prevention. The manufacturer of the propeller involved also concurred in publishing the report. This information is also presented here not only for its own value, but to alert those who are flying airplanes equipped with metal propellers that had been bent and straightened out or which had been cut down to be constantly aware of what little it takes to be the cause of an eventual propeller failure. The Metallurgist's Factual Report, Metallurgical Laboratory Report No. 69-19 is as follows: A.
FIG. 1. Appearance of the surface of the fracture in the propeller blade. Arrow "a" indicates the approximate origin of the fatigue fracture. X.43
ACCIDENT
Place: Ft. McCoy, Florida Date: October 29, 1967 Aircraft: Mooney M-20E, N-1302W NTSB No.: MIA 68-F-269 B.
COMPONENT EXAMINED
Piece of propeller blade from a Hartzell Propeller, Model HC-C2YK-1A; Blade Serial No. A58932F; Blade Material 2025-T6 aluminum alloy. C.
SUMMARY
Laboratory examination showed that the nucleus of the fatigue fracture in the propeller blade probably was at a corrosion pit in the camber surface. Numerous other corrosion pits associated with intergranular corrosion damage were found on the camber surface of the blade. Hardness tests on the blade material gave values typical of 2025-T6 aluminum alloy, which was the material specified for the blade. D.
DETAILS OF THE EXAMINATION
The piece of propeller blade examined was about six inches long and included the inboard surface of a chordwise fatigue fracture 9-":s in. from the tip. A visual examination of the fracture showed that a fatigue crack had originated on the camber surface of the blade approximately at the point indicated by arrow "a'1 in Fig. 1. The crack had propagated through about 75 percent of the cross-sectional area of the blade before the blade failed completely. After the failure occurred the fracture surface had been damaged by numerous scratches in the area of the fatigue origin. These scratches had obliterated surface markings that might have served to identify the exact point of crack nucleation. However, crack progression marks outside the scratched area indicated that the nucleus of the crack probably was at a 24
SEPTEMBER
1970
FIG. 2. Camber surface of the propeller blade in the area adjacent to the point on the fracture surface indicated by arrow "a", Fig. 1. Arrow "b" indicates a pit in the camber surface. Arrows "c" indicate some of the shallow grooves resulting from scratches on the fracture surface. X 20
corrosion pit (arrow "b" of Fig. 2) in the camber surface. Numerous other corrosion pits were found
on the camber surface of the blade, as shown in Fig. 3. An enlarged view of one of the pits is shown in Fig. 4. Metallographic examination of a section through the pit indicated by arrow "b'' in Fig. 2 showed that the pit was very shallow, as shown in Fig. 5. However, similar sections through other pits revealed considerable intcrgranular corrosion extending from the pits into the adjacent metal, as shown in Figs. 6 and 7. Also, some areas of intergranular corrosion without appreciable pitting (Fig. 8) were found. Although no evidence of intergranular corrosion in the plane of the fracture was observed in the section shown in Fig. 5, such evidence could have been destroyed by the scratches on the fracture surface. Hardness tests on specimens cut from the propeller blade gave an average value of 81 Rockwell K, which corresponds approximately to 110 Brinell. This is within the range of hardness normally found in properly heat-treated 2025-T6 aluminum-alloy material.
FIG. 5. Metal log raphic section through the pit indicated by arrow "b", Fig. 2. The top edge of the section intersects the camber surface of the blade and the right edge intersects the fracture surface. The deformed structure
FIG. 3.
Camber side of the blade near the fracture, show-
along the right edge is in the area where scratches were found on the fracture. Keller's etch. X 180
ing numerous corrosion pits (black spots) in the surface. X %
FIG. 6. Section through one of the corrosion pits on the camber surface of the blade. Unetched. X 150
FIG. 4. Appearance of one of the corrosion pits (arrow) in the camber surface at higher magnification than in Fig. 3. X 20
FIG. 7. Microstructure adjacent to one of the corrosion pits, showing the associated intergranular penetration.
Keller's etch. X 300
FIG. 8 Section through the camber surface of the blade in an area where intergranular attack had occurred without appreciable pitting. Keller's etch. X 540 SPORT AVIATION
scribe mark. When inspecting the propeller track, blades should be gently rocked to detect any possible looseness. Propeller blades exhibiting any looseness or ...
og aðrar kröfur, sem gerðar eru à tilskipun 1999/5/EC. Italiano [Italian]. Con la presente Wilibox dichiara che questo LigoDLB Propeller 2, LigoDLB Propeller 5, è conforme ai requisiti essenziali ed alle altre disposizioni pertinenti stabilite d
Much has been written about detecting metal fatigue through inspection for cracks. This should not give the false impression that the absence of cracks indicates ...
Apr 19, 1993 - the hub failed, releasing a propeller blade. The resultant ... Many assume dry air helps preserve metal. ... A propeller stored with its blades in a.
Warattah is a metal band: brutal, full and perfectly ..... and the success is a pleasure welcome. ... 'We all invite you to put your ears on the screaming. Warattah.
you didn't warn the owner of this twenty-five year old ... rent and future owners. This may result in a ..... Best deal in factory direct service. â¢. One year limited ...
Ãtape : on enlève les guides (a) après le vissage. Step : remove the installation templates (a) after having screwed. Ãtape : calage des barres transversales si le ...
of the Playboy which contains the fuselage and tail group - zinc chromated, landing gear, wheels, wing ribs, spars, plans, plus many fittings and other parts.
services and added repair or re- placement costs to users ... ble to your construction project, then consider ... the topic of designing for electrical system reliability.
mechanic handbooks, to guide you in identi- .... of new materials, and (4) damage that requires part replacement. ... is suspected. These advanced inspection ... manual prior to treatment of ferrous met- ... application of a solution of phosphoric.
og og goggagoggy. 105. â¢â¢ â¢â¢â¢..â¢Â°. #...... #â¢Â°â¢..â¢. # ........ #. 1". Overdrive. Em. 105. Acoustic 1 non gay ay ay ay ay ay ay ay ay ay ay. "O â¢â¢ ag at ay ay ay ay ay ay ay.
as polishing the 3"x3"x1" bar and the. 1" round bar roller may be difficult for you - you don't want to leave marks on the item that you are bend- ing. There may be ...
fatigue limit is exceeded, metal lite is being used up. Virtu- ally all metal .... the blade or running a pencil tip lightly along the blade ... Node Location from tip. 17".
way of life. We can take comfort in Oscar ... Turning a bolt into a nut moves it forward a given distance for each full turn. This is its pitch. If you have a 16-pitch bolt, one full turn will advance it 1/16 inch, or 16 full turns will move it 1 ...
(IPS) and location of the mass trim weights. (in degrees) from the engine index mark. The ACES manual provides an excellent guide to dynamically balancing ...
aircraft construction project when the builder is faced with a .... TYPE CERTIFICATE DATA SHEET NO. 3A12 ..... first page of the Cessna 172 data sheets which ...
As it is exposed to sunlight, wood darkens as a result ... particles. To remove more difficult stains, use a dampened soft cloth with either soapy luke warm water.
Australia and other ocean front countries. ... ous work, then an hour of rest. .... Jon Krapfl and Oiane Johnson with the U.S. Fish and Wildlife Service airboat at ...
I never really wanted to build or sell propellers. Looking back over the three years of development and testing that has resulted in the Airpower Propeller,.